Evaluating Morphological Characteristics and Filtration Performance of Electrospun Poly(Vinyl Alcohol)-Based Nanofiber Membranes for Capturing Particulate Matter; [ارزیابی ویژگ یهای ریخت شناختی و عملکرد فیلتراسیون مدیاهای نانولیفی بر پایه پلی وینیل الکل به منظور ربایش ذرات معلق در هوا]



Keyvani S ; Golbabaei F ; Neisiany RE ; Kalantary S ; Das O ; Foroushani AR
Source: Journal of Health and Safety at Work Published:2025

Abstract

Introduction: Polymer nanofiber filters have great potential for controlling particulate pollution due to their high filtration efficiency and low pressure drop. This study aimed to fabricate nanofiber membranes from a biodegradable polymer through solution electrospinning to address both health and environmental concerns, along with analyzing their morphological characteristics. The filtration performance of the prepared membranes was evaluated against different particle sizes under two air face velocities. Material and Methods: The nanofiber membranes were fabricated from aqueous poly(vinyl alcohol) (PVA) solutions at various concentrations from 5 to 6 w/v% under different process parameters. The morphological characteristics of the nanofibers were examined using field-emission scanning electron microscopy (FE-SEM), while structural properties such as basis weight and thickness were measured to estimate porosity. Filtration performance, including efficiency and pressure drop, was evaluated at two standard air face velocities (2.5 and 5.3 cm/s) using a media test system. In addition, the quality factor of the prepared membranes was calculated. Results: The electrospun nanofibers were uniform and bead-free, with the mean fiber diameters ranging from 106 to 151 nm. The filtration efficiencies were 95.72-99.92 % for sub-micron particles (0.3 and 0.5 µm), and 99.43-100 % for larger particles (1 and 3 µm). The pressure drop ranged from 67 to150 Pa at an air face velocity of 2.5 cm/s, and from 58 to150 Pa at an air face velocity of 5.3 cm/s. Conclusion: The 6 wt.% PVA nanofiber membrane electrospun at 15 kV, 0.5 mL/h, and 15 cm produced thinner fibers (approximately 106 nm) and exhibited higher efficiency for 0.3 µm particles (99.89 % and 99.92 % at 2.5 and 5.3 cm/s air face velocities, respectively). For this membrane with thinner fibers, the pressure drop increased from 67 to 150 Pa with rising the air face velocity. Copyright © 2025 The Authors.